| 摘要 |
<p>The present invention is related to a steel product of the weathering steel type, i.e. a product exhibiting increased corrosion resistance after having been exposed to the outside environment for a given time. According to the invention, the steel product is defined by a composition consisting of (in wt%) : - Carbon between 0.03 and 0.2, - Manganese between 0.5 and 2, - Copper between 0 and 0.5, - Ti between 0 and 0.1, - Cr between 0 and 0.5, - Nickel between 0 and 0.2, - Niobium between 0 and 0.1, - Nitrogen between 0 and 0.01, - Sulphur between 0 and 0.01, Phosphor between 0 and 0.01, - Aluminium higher than 0 and maximum 1.5, - Silicon between 0.25 and 1.5, the balance being Fe and accidental impurities, and wherein the sum of the Al and Si levels is higher than about 0.85wt%.</p> |