Tool for the cutting machining of workpieces and process for coating substrate bodies |
摘要 |
The invention relates to a tool having at least one layer of TixAl1-xN, where 0.2≦x≦0.8, which is composed of a plurality of laminar plies to give an overall layer thickness of 0.01 μm to 3 μm and which has crystallites having a size of ≦10 nm. To produce such a layer, by magnetron sputtering in an N2 atmosphere, Ti and Al are respectively released from separately arranged cathode targets, wherein the tool is moved past the cathode repeatedly at a speed which is such that in each case only a nanocrystalline layer forms upon this movement. |
申请公布号 |
US9126273(B2) |
申请公布日期 |
2015.09.08 |
申请号 |
US201314107268 |
申请日期 |
2013.12.16 |
申请人 |
KENNAMETAL INC |
发明人 |
Kohlscheen Joern |
分类号 |
C23C16/06;B23C5/16;C23C14/06;C23C14/35 |
主分类号 |
C23C16/06 |
代理机构 |
|
代理人 |
Gordon Matthew |
主权项 |
1. A tool for the cutting machining of workpieces, in particular for milling cast iron workpieces, wherein the tool comprises a coated cemented carbide body having at least one layer of TiAlN comprising crystallites, wherein the layer consists of TixAl1-xN, where 0.2≦x≦0.8, wherein the crystallites present in the TiAlN layer have a size of ≦10 nm and wherein the TiAlN layer further comprises a plurality of laminar plies to give an overall layer thickness of 0.01 μm to 3 μm. |