Method for continuous synthesis of metal oxide powders

摘要

A method for the rapid and continuous production of crystalline mixed-metal oxides from a precursor solution comprised of a polymerizing agent, chelated metal ions, and a solvent. The method discharges solution droplets of less than 500 μm diameter using an atomizing or spray-type process into a reactor having multiple temperature zones. Rapid evaporation occurs in a first zone, followed by mixed-metal organic foam formation in a second zone, followed by amorphous and partially crystalline oxide precursor formation in a third zone, followed by formation of the substantially crystalline mixed-metal oxide in a fourth zone. The method operates in a continuous rather than batch manner and the use of small droplets as the starting material for the temperature-based process allows relatively high temperature processing. In a particular embodiment, the first zone operates at 100-300° C., the second zone operates at 300-700° C., and the third operates at 700-1000° C., and fourth zone operates at at least 700° C. The resulting crystalline mixed-metal oxides display a high degree of crystallinity and sphericity with typical diameters on the order of 50 μm or less.

主权项

1. A method of producing a crystalline mixed-metal oxide comprising:
maintaining a precursor solution comprising a polymerizing agent, chelates, and a solvent, where the chelates comprise a which chelates agent chelating a plurality of metal ions, and where the precursor solution has a molar ratio of the chelating agent to the polymerizing agent of at least 1:1, and where the solvent is present in the precursor solution at a solvent weight percent, and where the precursor solution is maintained at a solution temperature less than the saturation temperature of the solvent; discharging a solution droplet into a first region of a reactor, where the first region of the reactor has a first temperature greater than the saturation temperature of the solvent, and where the solution droplet is a droplet of the precursor solution, and where the solution droplet has an equivalent spherical diameter of less than 500 μm, and where the solution droplet has a first momentum component, and where the solution droplet comprises a polymerizing agent portion, a chelates portion, and a solvent portion, providing a translational distance in the first region of the reactor such that the first momentum component of the solution droplet maintains the solution droplet in the first region of the reactor for a time sufficient to evaporate at least 50% of the solvent portion from the solution droplet and transform the solution droplet to a gel droplet having a second momentum component; permitting the second momentum component to displace the gel droplet to a second region of the reactor having a second temperature, and providing a translational distance in the second region of the reactor such that the second momentum component maintains the gel droplet in the second region of the reactor for a time sufficient to generate polymer molecules, where the polymer molecules comprise some quantity of the polymerizing agent portion and some quantity of the chelates portion, and where the polymer molecules comprise organics, and transforming the gel droplet to a metal organic foam material having a third momentum component, where the metal organic foam material comprises the polymer molecules; permitting the third momentum component to displace the metal organic foam material to a third region of the reactor having a third temperature and contacting the metal organic foam material with gaseous oxygen in the third region of the reactor, where the third temperature is sufficient to decompose a quantity of the organics, and providing a translational distance in the third region of the reactor such that the third momentum component maintains the metal organic foam material in the third region of the reactor for a time sufficient to decompose the quantity of organics and transform the metal organic foam material to a plurality of initial metal oxide particles having a fourth momentum component; permitting the fourth momentum component to displace the plurality of initial metal oxide particles to a fourth region of the reactor having a fourth temperature and contacting the plurality of initial metal oxide particles with additional gaseous oxygen in the fourth region of the reactor, where the fourth temperature is sufficient to transform some portion of the plurality of initial metal oxide particles to a plurality of substantially crystalline mixed-metal oxide particles, and providing a translational distance in the fourth region of the reactor such that the fourth momentum component maintains some portion of the plurality of initial metal oxide particles in the fourth region of the reactor for a time sufficient to transform the some portion of the plurality of initial metal oxide particles to the plurality of substantially crystalline mixed-metal oxide particles, thereby producing the crystalline mixed-metal oxide.