Cathode active material precursor particle, method for producing thereof and method for producing cathode active material for lithium secondary battery

摘要

A cathode active material precursor particle, a method for producing thereof and a method for producing cathode active material for a lithium secondary battery. The cathode active material precursor particle is capable of forming a cathode active material for a lithium secondary battery including a lithium composite oxide having a layered rock salt structure through lithium incorporation. The particles are characterized by the cathode active material precursor particle being formed into a substantially spherical shape and includes therein a large number of voids in a substantially uniform manner; and the cathode active material precursor particle has: an average particle diameter D50 of 0.5 to 5 μm; a specific surface area of 3 to 25 m2/g; and a relative tap density, which is a value obtained by dividing a tap density by a theoretical density of a material constituting the cathode active material precursor particle, of 0.25 to 0.4.

主权项

1. A production method for a cathode active material for a lithium secondary battery comprising a lithium composite oxide having a layered rock salt structure,
the method comprising: a granulation step of forming a granule, which comprises a large number of plate-like particles of a transition metal hydroxide constituting a main raw material for the lithium composite oxide and comprises therein a large number of voids in a substantially uniform manner; and a thermal treatment step of thermally treating the granule to form a cathode active material precursor particle, which is formed into a substantially spherical shape and comprises therein a large number of voids in a substantially uniform manner, and has an average particle diameter D50 of 0.5 to 5 μm, a specific surface area of 3 to 25 m2/g, and a relative tap density, which is a value obtained by dividing a tap density by a theoretical density of a material constituting the cathode active material precursor particle, of 0.25 to 0.4; a forming step of forming a large number of the cathode active material precursor particles into a predetermined shape to provide a green product; and a sintering step of sintering the green product to generate the lithium composite oxide, wherein a lithium compound is added to the cathode active material precursor particle after the cathode active material precursor particle is thermally treated and before the green product is sintered to generate the lithium composite oxide.