Electrocatalyst for electrochemical conversion of carbon dioxide

摘要

An electrocatalyst for the electrochemical conversion of carbon dioxide to hydrocarbons is provided. The electrocatalyst for the electrochemical conversion of carbon dioxide includes copper material supported on carbon nanotubes. The copper material may be pure copper, copper and ruthenium, copper and iron, or copper and palladium supported on the carbon nanotubes. The electrocatalyst is prepared by dissolving copper nitrate trihydrate in deionized water to form a salt solution. Carbon nanotubes are then added to the salt solution to form a suspension, which is then heated. A urea solution is added to the suspension to form the electrocatalyst in solution. The electrocatalyst is then removed from the solution. In addition to dissolving the copper nitrate trihydrate in the deionized water, either iron nitrate monohydrate, ruthenium chloride or palladium chloride may also be dissolved in the deionized water to form the salt solution.

主权项

1. A method of making an electrocatalyst for electrochemical conversion of carbon dioxide, comprising the steps of:
dissolving copper nitrate trihydrate in deionized water to form a salt solution; adding carbon nanotubes to the salt solution to form a suspension; heating the suspension; adding a urea solution to the suspension to form an electrocatalyst in solution, the electrocatalyst comprising copper material supported on the carbon nanotubes; cooling the solution to room temperature; removing the electrocatalyst from the solution by centrifuging the solution to separate the electrocatalyst out of the solution; washing and drying the electrocatalyst at a temperature of about 110° C.; and calcining the washed and dried electrocatalyst at a temperature of about 450° C. for about four hours in an argon gas flow.