RESIN FOAM AND FOAM MATERIAL |
摘要 |
A resin foam having a repulsive stress when compressed by 80% of 1.0 to 9.0 N/cm2, a maximum breaking strength of 1.0 to 10.0 MPa, and a ratio of the maximum breaking strength to a breaking strength in a direction orthogonal to a maximum breaking strength direction (maximum breaking strength/breaking strength in the direction orthogonal to the maximum breaking strength direction) of 1.0 to 5.0. The maximum breaking strength is defined as: a resin foam in a sheet form is measured for a breaking strength in an arbitrary direction in the horizontal direction of the sheet; next, the arbitrary direction is rotated about an axis by 10° intervals to measure a breaking strength in each direction; a direction where the highest breaking strength is measured is defined as the maximum breaking strength direction; and a breaking strength in the maximum breaking strength direction is defined as the maximum breaking strength. |
申请公布号 |
US2015218422(A1) |
申请公布日期 |
2015.08.06 |
申请号 |
US201314403822 |
申请日期 |
2013.05.21 |
申请人 |
NITTO DENKO CORPORATION |
发明人 |
Kato Kazumichi;Saitou Makoto;Hatanaka Itsuhiro;Kodama Kiyoaki |
分类号 |
C09J7/02;C09J133/00;C08J9/12 |
主分类号 |
C09J7/02 |
代理机构 |
|
代理人 |
|
主权项 |
1. A resin foam having a repulsive stress when compressed by 80% of 1.0 to 9.0 N/cm2, a maximum breaking strength as defined below of 1.0 to 10.0 MPa, and a ratio of the maximum breaking strength as defined below to a breaking strength in a direction orthogonal to a maximum breaking strength direction (maximum breaking strength/breaking strength in the direction orthogonal to the maximum breaking strength direction) of 1.0 to 5.0,
wherein the maximum breaking strength is defined as follows: a resin foam in a sheet form is measured for a breaking strength in an arbitrary direction in a horizontal direction of the sheet; next, the arbitrary direction is rotated about an axis by 10° intervals to measure a breaking strength in each direction; a direction where the highest breaking strength is measured is defined as the maximum breaking strength direction; and a breaking strength in the maximum breaking strength direction is defined as the maximum breaking strength. |