Positive electrode active material for lithium-ion battery, positive electrode for lithium-ion battery, and lithium-ion battery |
摘要 |
The present invention provides a positive electrode active material for lithium ion battery having good rate characteristics. The positive electrode active material for lithium ion battery has a layer structure expressed by a composition formula: Lix(NiyM1-y)Oz, wherein M represents Mn and Co, x represents 0.9 to 1.2, y represents 0.6 to 0.9, and z represents 1.8 to 2.4. The positive electrode active material has a particle size ratio D50P/D50 of 0.60 or more, wherein D50 is the average secondary particle size of the positive electrode active material powder, and D50P is the average secondary particle size of the positive electrode active material powder after pressing at 100 MPa. The positive electrode active material contains 3% or less particles having a particle size of 0.4 μm or less in terms of the volume ratio after pressing at 100 MPa. |
申请公布号 |
US9090481(B2) |
申请公布日期 |
2015.07.28 |
申请号 |
US201113582087 |
申请日期 |
2011.02.21 |
申请人 |
JX Nippon Mining & Metals Corporation |
发明人 |
Satoh Hirohito |
分类号 |
H01M4/131;C01G53/00;H01M4/505;H01M4/525;H01M10/0525 |
主分类号 |
H01M4/131 |
代理机构 |
Nields, Lemack & Frame, LLC |
代理人 |
Nields, Lemack & Frame, LLC |
主权项 |
1. A positive electrode active material for a lithium ion battery having a layer structure expressed by a composition formula:
Lix(NiyM1-y)Oz, wherein M represents Mn and Co, x represents 0.9 to 1.2, y represents 0.6 to 0.9, and z represents 1.8 to 2.4, the positive electrode active material having a particle size ratio D50P/D50 of 0.60 or more, wherein D50 is the average secondary particle size of the positive electrode active material in powder form, and D50P is the average secondary particle size of the positive electrode active material in powder form after pressing at 100 MPa, and the positive electrode active material containing 3% or less particles having a particle size of 0.4 μm or less in terms of a volume ratio after pressing at 100 MPa. |