发明名称 |
Method for the establishment of a crack resistant epoxy paint coat and paint compositions suitable for said method |
摘要 |
The present invention relates to a method for the establishment of a crack resistant epoxy paint coat and paint compositions suitable for said method. The method is developed for use in ballast tanks e.g. a ballast tank of a vessel. The method involves the steps: (i) applying a paint composition comprising an epoxy-based binder system onto the surface thereby forming a curable paint film on the surface, and (ii) allowing the curable paint film to cure thereby forming the epoxy paint coat. The paint composition has a viscosity of at the most 140 KU, when ready to be applied. The paint composition comprises 35-80% by solids volume of the paint of an epoxy-based binder system having a ratio between the hydrogen equivalents and the epoxy equivalents in the range of 20:100 to 120:100. The paint composition furthermore comprises 0.5-30% by solids volume of the paint of one or more fibers. The fibers have an average length, of at the most 250 μm. |
申请公布号 |
US9080062(B2) |
申请公布日期 |
2015.07.14 |
申请号 |
US201414320063 |
申请日期 |
2014.06.30 |
申请人 |
HEMPEL A/S |
发明人 |
Scheibel Kim;Kahle Jorn;Pedersen Michael Stanley;Pedersen Lars Thorslund |
分类号 |
B05D5/00;C09D163/00;C09D5/02;C09D7/12;C09D163/04;C08K7/04;C08K7/02;C08K7/06 |
主分类号 |
B05D5/00 |
代理机构 |
Birch, Stewart, Kolasch & Birch, LLP |
代理人 |
Birch, Stewart, Kolasch & Birch, LLP |
主权项 |
1. A paint composition having a viscosity of at the most 140 KU at 30° C. and comprising:
35-80% by solids volume of the paint of an epoxy-based binder system having a ratio between the hydrogen equivalents and the epoxy equivalents in the range of 60:100 to 120:100, wherein the epoxy-based binder system comprises (a) one or more epoxy resins selected from the group consisting of bisphenol A and bisphenol F and (b) one or more polyamidoamine or Mannich base curing agent, and 0.5-30% by solids volume of the paint of one or more mineral fibres having an average length, of at most 250 μm. |