Process for production of water-absorbent resin

摘要

A purpose of the present invention is to reduce odor of a water-absorbent resin during absorption of water. Such the invention is attained by a process for production of a water-absorbent resin by subjecting a water-soluble ethylenically unsaturated monomer to reversed-phase suspension polymerization. The process comprises the following steps (A) to (C): (A) adding an aqueous solution of water-soluble ethylenically unsaturated monomer to a petroleum hydrocarbon dispersion medium to disperse the aqueous solution in the dispersion medium; (B) adding a surfactant to the emulsion to further disperse the emulsion; and (C) performing the reversed-phase suspension polymerization using a water-soluble radical polymerization initiator, optionally in the presence of an internal-crosslinking agent.

主权项

1. A process for production of a water-absorbent resin by subjecting a water-soluble ethylenically unsaturated monomer to reversed-phase suspension polymerization, comprising the following steps of:
(A) adding an aqueous solution of water-soluble ethylenically unsaturated monomer to a petroleum hydrocarbon dispersion medium to disperse the aqueous solution in the dispersion medium, (B) adding a surfactant to the emulsion to further disperse the monomer in the emulsion, and (C) performing the reversed-phase suspension polymerization using a water-soluble radical polymerization initiator optionally in the presence of an internal-crosslinking agent, wherein the surfactant is selected from the group consisting of sorbitan fatty acid ester, polyglycerin fatty acid ester, sucrose fatty acid ester, and combinations thereof, wherein the petroleum hydrocarbon dispersion medium is selected from the group consisting of aliphatic hydrocarbons, alicyclic hydrocarbons having 6 to 7 carbon atoms, and a mixture thereof, wherein the aqueous solution of ethylenically unsaturated monomer is added to and dispersed in the petroleum hydrocarbon dispersion medium in the presence of a polymeric dispersion agent in the step (A), and wherein the polymeric dispersion agent is selected from the group consisting of maleic anhydride modified polyethylene, maleic anhydride modified polypropylene, maleic anhydride modified ethylene-propylene copolymer, oxidized polyethylene, oxidized polypropylene, and combinations thereof.