Method for producing organopolysiloxane emulsion composition

摘要

A method for producing an organopolysiloxane emulsion composition, which enables the organopolysiloxane to be formed with a high viscosity in a short period of time, and suppresses the amount of octamethylcyclotetrasiloxane (D4) to not more than 3,000 ppm. Specifically, a method for producing an organopolysiloxane emulsion which includes emulsifying a mixture containing an organopolysiloxane represented by formula: HO(R12SiO)nH and having a D4 content of not more than 1,000 ppm, a nonionic surfactant, an anionic surfactant, and water, and subjecting the obtained emulsion composition to emulsion polymerization, thus preparing the emulsion composition.

主权项

1. A method for producing an organopolysiloxane emulsion composition, the method comprising:
(I) preparing a first emulsion composition by performing emulsification of a mixture comprising:
(A) 100 parts by mass of an organopolysiloxane represented by general formula (1) shown below, and having an octamethylcyclotetrasiloxane content of not more than 1,000 ppm,
HO(R12SiO)nH  (1) wherein each R1 independently represents a hydrogen atom or a substituted or unsubstituted hydrocarbon group of 1 to 20 carbon atoms, and n represents a number that yields a viscosity at 25° C. for the organopolysiloxane of 3,000 to 100,000 mm2/s,
(B) 1 to 100 parts by mass of a nonionic surfactant,(C) 1 to 100 parts by mass of an anionic surfactant, provided that a mass ratio of component (B):component (C) is within a range from 20:80 to 55:45, and
(D-1) 1 to 10 parts by mass of water; and (II) subjecting the first emulsion composition to emulsion polymerization, either without adding any water, or following addition of (D-2) not more than 100,000 parts by mass of water, the emulsion polymerization performed at a temperature of less than 40° C., in presence of an acid catalyst (E) (although the acid catalyst is unnecessary in those cases where the anionic surfactant (C) has a catalytic action), thus preparing a target emulsion composition, in which a viscosity at 25° C. of the organopolysiloxane generated in a polymerization time of not more than 15 hours is 300,000 mPa·s or greater, and an amount of octamethylcyclotetrasiloxane contained in the organopolysiloxane is not more than 3,000 ppm.