Process for making silver powder particles with very small size crystallites

摘要

The process for making silver powder particles with very small size crystallites uses a combination of gum arabic and maleic acid with the reduction of a silver salt with ascorbic acid. Silver thick film paste containing these silver powder particles can be used in electronic applications to form electrodes for semiconductor devices and, in particular, solar cells.

主权项

1. A process for making silver powder particles, said process comprising:
(a) preparing an acidic aqueous silver salt solution comprising a water soluble silver salt dissolved in deionized water; (b) preparing an acidic aqueous reducing and particle modifier solution comprising:
(i) a reducing agent selected from the group consisting of ascorbic acid, ascorbates and mixtures thereof;(ii) nitric acid;(iii) maleic acid; and(iv) deionized water, wherein the pH of said acidic aqueous reducing and particle modifier solution is adjusted by the addition of a base to between 2.5 and 6; (c) maintaining said acidic aqueous silver salt solution and said acidic reducing and surface morphology modifier solution at the same temperature, wherein said temperature is in the range of 10° C. to 65° C., while stirring each said solution during and after preparation; (d) adding said acidic aqueous silver salt solution to said acidic aqueous reducing and particle modifier solution while stirring to make a reaction mixture and maintaining the temperature of said reaction mixture at said temperature of (c), wherein said silver powder particles precipitate and are contained within the resulting final aqueous solution; and (e) increasing the temperature of said final aqueous solution to a temperature in the range of 65° C. to 80° C. while continuing stirring;one or both of said acidic aqueous silver salt solution and said acidic aqueous reducing and particle modifier solution further comprising gum arabic and said silver powder particles comprising crystallites of size less than or equal to 32 nm as determined by X-ray diffraction and the Scherrer formula; and said silver powder particles having a d50 in the range of 0.5 to 3.5 μm.