Method of production of hot coil for line pipe

摘要

The present invention provides a hot coil for line pipe use which can reduce deviation in ordinary temperature strength and improve low temperature toughness despite the numerous restrictions in production conditions due to the coiling step and provides a method of production of the same, specifically makes the steel plate stop for a predetermined time between rolling passes in the recrystallization temperature range and performs cooling by two stages after hot rolling so as to thereby make the steel structure at the center part of plate thickness and effective crystal grain size of 3 to 10 μm, make the total of the area ratios of bainite and acicular ferrite 60 to 99%, and make the absolute value of A-B 0 to 30% when the totals of the area ratios of bainite and acicular ferrite at any two portions are designated as respectively A and B.

主权项

1. A method of production of hot coil for line pipe use characterized by heating a steel slab which has a chemical composition which contains, by mass %,
C: 0.03 to 0.10%, Si: 0.01 to 0.50%, Mn: 0.5 to 2.5%, P: 0.001 to 0.03%, S: 0.0001 to 0.0030%, Nb: 0.0001 to 0.2%, Al: 0.0001 to 0.05%, Ti: 0.0001 to 0.030%, and B: 0.0001 to 0.0005% and which has a balance of iron and unavoidable impurities to 1000 to 1250° C., then hot rolling it, during which making a draft ratio in a recrystallization temperature range 1.9 to 4.0 and making the steel plate in the middle of the hot rolling stop at least once between rolling passes in the recrystallization temperature range for 100 to 500 seconds, and cooling the obtained hot rolled steel plate divided between a front stage and a back stage, during which, in the front stage cooling, cooling by a cooling rate of 0.5 to 15° C./sec at a center part of plate thickness of the hot rolled steel plate until a surface temperature of said hot rolled steel plate becomes 600° C. from the cooling start temperature of the front stage, and, in the back stage cooling, cooling by a cooling rate which is faster than the front stage at the center part of plate thickness of the hot rolled steel plate, and coiling the steel plate, after said back stage cooling, at 450 to 600° C.