Method for producing hot rolled hollow sections having a rectangular cross-section and small edge radii

摘要

In a method for producing hot-rolled sections of steel with a rectangular or square cross-section, a substantially round pipe blank produced seamlessly by hot rolling or cold finished and welded and having a defined nominal outside diameter is initially produced and then formed at a forming temperature into a hollow section having the required cross-section, with visible edges C1 and C2 of the hollow section having a value ≦1.5×t (t=wall thickness). The pipe blank has a nominal outer diameter determined from a reduction ratio of the pipe blank to be achieved and the hollow section dimensions to be achieved, wherein the reduction ration lies within a range of −2% to −13% and is determined according to the following formula:
Reduction ratio R[%]=[(2×(H+B))−π×D]×100%/[2×(H+B)].

主权项

1. A method for producing a hot rolled hollow section made of steel and having a rectangular or square cross section, comprising:
producing a substantially round pipe blank having a defined nominal outer diameter by seamless hot-rolling or cold-finishing and welding; forming the pipe blank in a rolling mill at a forming temperature into a hollow section having visible edges defined by a value of ≦1.5×t, wherein t is a wall thickness of the hollow section; and determining the nominal outer diameter of the pipe blank as a function of a reduction ratio to be achieved of the pipe blank and dimensions to be achieved of the hollow section, wherein the reduction ratio lies within a range of −2% to −13% and is determined by the formula:
Reduction ratio R [%]=[(2×(H+B))−π×D]×100%/[2×(H+B)], wherein H is a height of the hollow section, B is a width of the hollow section, D is an outer diameter of the pipe blank at the forming temperature and before the forming step.