主权项 |
1. A method for producing a metal-oxide sintered body, the method comprising the steps of:
a) mixing ZrO2 with one or more materials serving to stabilize ZrO2, and selected from the group consisting of Al2O3, Y2O3, CeO2, MgO, SiO2, Ta2O5 and ThO2, followed by heat treatment at a temperature equal to or higher than ½ of the melting temperature of ZrO2, to prepare stabilized zirconia (ZrO2) powder; b) heat-treating a composition having a formula of Mn0.27Fe0.16Ni0.27Y0.2Al0.1O1.5 at a temperature ranging from 1,000° C. to 1,500° C. for 1-5 hours to prepare powder; and c) mixing the powder prepared in step a) with the powder prepared in step b) to prepare a mixture, and heat-treating the mixture at a temperature ranging from 1,100° C. to 1,700° C. for 30 minutes to 2 hours, thereby producing a sintered metal-oxide having a formula of Mn0.108Fe0.064Ni0.108Y0.28Al0.04Zr0.402O1.701. |