<p>Provided is a method for making epoxy asphalt mixture capable of solving the problems of clotting generated by epoxy resin and early curing time resulting from high reactivity of epoxy resin and the curing agent. When the epoxy asphalt mixture is produced, the host crystal and the curing agent shall be respectively packaged. The packaged host agent and the curing agent are put into a bituminous mixture manufacturing machine. The host crystal is made by 100 parts by weight of epoxy resin, 0.5-10 parts by weight of mixed iron oxide pigment, and 4-10 parts by weight of talcum powder relative to epoxide equivalent400-600 and with the melting point below 70 DEG C. The curing agent is 24-36 parts by weight of aliphatic series primary amine with iodine value ranging from 35 to 60.</p> |