A high strength galvanized steel sheet is provided comprising steel containing C: 0.06% or more and 0.20% or less, Si: less than 0.50%, Mn: 0.5% or more and less than 2.0%, P: 0.05% or less, S: 0.02% or less, Al: 0.60% or more and 2.00% or less, N: less than 0.004%, Cr: 0.10% or more and 0.40% or less and B: 0.003% or less, satisfying the relationships 0.8≦Mneq≦2.0 and Mneq+1.3[% Al]≧2.8, and a microstructure containing a ferrite phase and a second phase whose volume fraction is 15% or less, the second phase having a martensite phase whose volume fraction is 3% or more, a retained austenite phase whose volume fraction is 3% or more and a sum of the volume fractions of a pearlite phase and a bainite phase being equal to or less than the volume fraction of the martensite phase and the volume fraction of the retained austenite phase. |
| 主权项 |
1. A high strength galvanized steel sheet having excellent uniform elongation and zinc coatability, which comprises steel having a chemical composition containing, by mass %, C: 0.06% or more and 0.20% or less, Si: less than 0.50%, Mn: 0.5% or more and 1.87% or less, P: 0.05% or less, S: 0.02% or less, Al: 0.60% or more and 2.00% or less, N: less than 0.004%, Cr: 0.10% or more and 0.40% or less, B: 0.003% or less (including 0%) and the balance being Fe and inevitable impurities, where Mneq defined below satisfies the relationships 0.8≦Mneq≦2.0 and Mneq+1.3[% Al]≧2.8, and having a microstructure containing a ferrite phase as a parent phase and a second phase whose volume fraction is 15% or less, the second phase having a martensite phase whose volume fraction is 3% or more, a retained austenite phase whose volume fraction is 3% or more and a sum of the volume fractions of a pearlite phase and a bainite phase which is equal to or less than the volume fraction of the martensite phase and which is equal to or less than the volume fraction of the retained austenite phase, and a galvanizing layer on the surface of the steel sheet,
the steel sheet having a tensile strength of 440 MPa or more and less than 590 MPa and a uniform elongation of 24% or more:
Mneq=[% Mn]+1.3[% Cr]+4[% P]+150[% B], where [% Mn], [% Cr], [% P] and [% B] respectively denote the contents by mass % of Mn, Cr, P and B in the chemical composition of the steel, and where [% Al] described above also denotes the content by mass % of Al in the chemical composition of the steel. |