FIELD: metallurgy.SUBSTANCE: invention relates to metallurgy, in particular to brazing filler for high temperature brazing of stainless steel. Brazing filler powder on Fe-Cr base for high temperature brazing of the base metal out of stainless steel contains in wt %: Cr from 11 to 35, Ni up to 30, Cu from 5 to 20, Si from 2 to 10, P from 4 to 10, Mn up to 10, Fe - rest, at least 20. If Si content is below or equal to 6 wt %, P content is over 8 wt %, and at P content below or equal to 8 wt %, Si content is over 6 wt %.EFFECT: brazing filler makes brazed joint with high strength and good corrosion resistance.15 cl, 2 tbl, 5 ex |