Titanium sheet covered with protective film superior in high temperature oxidation resistance and high temperature salt damage resistance, automobile exhaust system using same, and methods of production of same

摘要

The present invention provides a titanium sheet covered with a protective film superior in high temperature oxidation resistance and high temperature salt damage resistance and a method of production of the same and an automobile exhaust system using the same. The titanium sheet covered with a protective film is formed on its surface with a protective film of a thickness of 1 to 100 μm where flake-shaped metal Al with an average thickness of 0.1 to 5 μm and average width or average length of 1 to 50 μm or grain-shaped metal Al with an average size of 0.1 to 30 μm is dispersed in 20 to 60 mass % silicone resin or silicone grease and comprised of Si: 15 to 55 mass % and C: 10 to 45 mass % and having a balance of unavoidable impurities. Preferably the titanium sheet of the substrate contains one or both of 0.5 to 2.1 mass % of Cu and 0.4 to 2.5 mass % of Al. The method of production is to brush or spray the above composition of a silicone resin on a titanium sheet to form a protective film and heat it at 150 to 300° C. for 5 to 60 minutes.

主权项

1. A method of production of a titanium sheet covered with a protective film superior in high temperature oxidation resistance and high temperature salt damage resistance, the method comprising coating a silicone resin or silicone grease prepared to contain Si: 15 to 55 mass %, C: 10 to 45 mass % and a metal Al alloy on a titanium sheet by brushing or spraying to form a protective film on the surface of the titanium sheet, and heating said titanium sheet covered with the protective film at 600° C. to 800° C. for 30 minutes to 10 hours to form at least one or more compounds of Al2O3, SiO2, Ti—Si and Ti-Al at the interface of the protective film and titanium substrate,
wherein the metal Al alloy of a thin flake shape with an average thickness of 0.1 to 5 μm and an average width or average length of 1 to 50 μm or of a grain shape with an average particle size of 0.1 to 30 μm is dispersed in the silicone resin in a ratio of 10 to 40 mass %, said metal Al alloy being one or more of an Al—Si alloy comprised of Si: 10.5 to 30 mass % and having a balance of Al and unavoidable impurities, an Al—Mg alloy comprised of Mg: 0.3 to 13.0 mass % and having a balance of Al and unavoidable impurities, and an Al—Mg—Si alloy comprised of Mg: 0.3 to 13.0 mass % and Si: 0.3 to 13.0 mass % and having a balance of Al and unavoidable impurities.