Optical module

摘要

An optical module is provided that includes a Faraday rotator having a Verdet constant at a wavelength of 1.06 μm of at least 0.27 min/(Oe·cm), a first hollow magnet disposed on the outer periphery of the Faraday rotator, and second and third hollow magnet units disposed so as to sandwich the first hollow magnet on the optical axis. The second and third hollow magnet units include 2 or more magnets equally divided in a direction of 90 degrees relative to the optical axis. A magnetic flux density B (Oe) applied to the Faraday rotator is in the range of 0.5×104≦B≦1.5×104. The Faraday rotator is disposed on a sample length L (cm) in the range of 0.70≦L≦1.10, and has an external diameter D (cm) in the range of 0.20≦D≦0.60.

主权项

1. A process of producing an optical module comprising:
a Faraday rotator having a Verdet constant at a wavelength of 1.06 μm of at least 0.27 min/(Oe·cm); a first hollow magnet disposed on the outer periphery of the Faraday rotator; and a second hollow magnet unit and a third hollow magnet unit, the second and third hollow magnet units disposed so as to sandwich the first hollow magnet on an optical axis, each of the second and third hollow magnet units comprising 2 or more magnets equally divided in a direction of 90 degrees relative to the optical axis, the Faraday rotator applied thereto a magnetic flux density B (Oe) in the range of Formula (1) below, the Faraday rotator having a length L (cm) along the optical axis in the range of Formula (2) below, and the Faraday rotator having an external diameter D (cm) in the range of Formula (3) below
0.5×104≦B≦1.5×104  (1)0.70≦L≦1.10  (2)0.20≦D≦0.60  (3) wherein the Faraday rotator comprises an oxide represented by Formula (I) below in at least 99% by weight:
(TbxR1-x)2O3  (I), wherein 0.5≦x≦1.0, and R comprises at least one element selected from the group consisting of scandium, yttrium, and lanthanoid elements other than Tb, the process comprising the steps of: grinding an outer peripheral face of the Faraday rotator by 1.0 mm or greater to reduce the external diameter D to the diameter of Formula (3); and polishing opposite end faces of the Faraday rotator by 0.5 mm or greater for each face to reduce the length to the length L of Formula (2).