发明名称 |
非晶质铁基合金及其充磁退火方法;AMORPHOUS FE-BASED ALLOY AND MAGNETIC ANNEALING METHOD THEREOF |
摘要 |
一种非晶质铁基合金及其充磁退火方法。提供非晶质铁基合金胚,其中非晶质铁基合金胚包含78重量百分比至82重量百分比之铁、2重量百分比至9重量百分比之矽、10重量百分比至17重量百分比之硼、大于0重量百分比至1重量百分比之碳以及其他不可避免之杂质。进行充磁退火步骤,其中充磁退火步骤持续0.5小时至2小时,且充磁退火步骤包含利用充磁电流为800安培至1600安培以及加热温度为300℃至350℃,以形成非晶质铁基合金。 An amorphous Fe-based alloy and a magnetic annealing method thereof are described. An amorphous Fe-based alloy billet is provided, in which the billet includes iron in a range from 78wt% to 82wt%, silicon in a range from 2wt% to 9wt%, boron in a range from 10wt% to 17wt%, carbon in a range from greater than 0wt% to 1wt% and unavoidable impurities. A magnetic annealing step is performed to form the amorphous Fe-based alloy, in which the magnetic annealing step lasts 0.5 hour to 2 hours and includes using a magnetizing current ranged from 800A to 1600A and a heating temperature ranged from 300℃ |
申请公布号 |
TW201514323 |
申请公布日期 |
2015.04.16 |
申请号 |
TW102136608 |
申请日期 |
2013.10.09 |
申请人 |
中国钢铁股份有限公司 CHINA STEEL CORPORATION |
发明人 |
陈伯宇 CHEN, POYU;杨哲人 YANG, JERREN;蔡明钦 TSAI, MINGCHIN;李欣怡 LEE, HSINYI |
分类号 |
C22C45/02(2006.01);H01F1/153(2006.01);H01F41/02(2006.01) |
主分类号 |
C22C45/02(2006.01) |
代理机构 |
|
代理人 |
蔡坤财李世章 |
主权项 |
|
地址 |
高雄市小港区中钢路1号 TW |