Metal nanowires with high linearity, method for producing the metal nanowires and transparent conductive film including the metal nanowires

摘要

Metal nanowires with high linearity can be produced using metal salts at a relatively low temperature. A transparent conductive film can be formed using the metal nanowires. Particularly, the transparent conductive film has high transmittance, low sheet resistance, and good thermal, chemical and mechanical stability. The transparent conductive film has a high electrical conductivity due to the high linearity of the metal nanowires. The metal nanowires take up 5% or less of the volume of the transparent conductive film, ensuring high transmittance of the transparent conductive film. Furthermore, the metal nanowires are useful as replacements for existing conductive materials, such as ITO, conductive polymers, carbon nanotubes and graphene. The metal nanowires can be applied to flexible substrates and other various substrates due to their good adhesion and high applicability to the substrates. Moreover, the metal nanowires can find application in various fields, such as displays and solar cell devices.

主权项

1. A method for producing metal nanowires with high linearity, the method comprising:
(a) mixing a polymeric material and a reducing agent in a solvent and stirring the mixture to prepare a first mixed solution; (b) adding a first metal salt to the first mixed solution to prepare a second mixed solution containing metal seeds formed therein; and (c) adding a second metal salt to the second mixed solution and reacting to form metal nanowires, wherein the solvent is a mixture of distilled water and at least one solvent selected from diethanolamine and triethanolamine, the polymeric material is selected from polymethyl methacrylate, polyvinyl butyral, polyethyl methacrylate and mixtures thereof, each of the polymers having a molecular weight of 800,000 to 2,000,000, the reducing agent is selected from sodium borohydride, sodium hydroxide, sodium phosphinate monohydrate, ammonium hydroxide, potassium bromide, cetyltrimethylammonium bromide and mixtures thereof, and the first metal salt and the second metal salt are each independently an acetate, nitrate, chloride or sulfate salt comprising a metal selected from Cu and Ni; and the first metal salt and the second metal salt are different salts of the same metal.