| 摘要 |
A method of thermomechanical shaping a final product with very high strength including the steps of: providing a coated hot-rolled and/or cold-rolled steel strip or sheet including (all percentages in wt. %): 0.04%<carbon<0.5%, 0.5%<manganese<3.5%, silicon<1.0%, 0.01%<chromium<1%, titanium<0.2%, aluminum<0.2%, phosphorus<0.1%, nitrogen<0.015% N, sulphur<0.05%, boron<0.015%, unavoidable impurities, balance iron, the steel being coated with a zinc alloy coating layer, wherein the zinc alloy includes 0.3-4.0% Mg and 0.05-6.0% Al; optionally at most 0.2% of one or more additional elements; unavoidable impurities; the remainder being zinc; cutting the steel sheet to obtain a steel sheet blank; thermomechanical shaping of the steel sheet blank to a final product with its final properties. |