A method of manufacturing shoe insoles, comprises steps of: step 1, making a resin mixture by mixing a resin and a hardening agent in a container; step 2, impregnating a glass fiber cloth with the resin mixture in step 1; step 3, cutting the glass fiber cloth impregnated in step 2 according to a pre-determined shape of a half insole or of an insole; step 4, hot-press forming a product by adding the glass fiber cloth cut in step 3 to a pre-heated mold, and heat pressing the glass fiber cloth to obtain the product of a shoe insole. A shoe insole manufactured according to the above method and a shoe comprising the same are also disclosed, involving high strengths, small thicknesses, light weights, resistances to moisture as well as hydrolysis, longtime molding effects, a strong weatherability and a good balance, and facilitating the standardization of shoe manufacturing. |
| 主权项 |
1. A method of manufacturing shoe insoles, wherein, the method comprises steps as follows:
step 1, stirring a resin mixture, wherein, the resin mixture includes resin, 0.1%-80% of hardening agent, 1%-30% of low shrinkage agent, 0.5%-10% of thickening agent and 0.5%-10% of releasing agent, the resin is any of unsaturated resin, epoxy resin, vinyl resin and phenolic resin, and the resin is stirred to mixed with the hardening agent, low shrinkage agent, thickening agent and releasing agent in a container; step 2, impregnating a glass fiber cloth by saturating the glass fiber cloth with the resin mixture stirred in step 1; step 3, trimming the glass fiber cloth by cutting the glass fiber cloth impregnated in step 2 according to a pre-determined shape of a half insole or of an insole; step 4, hot-press forming a product by adding the glass fiber cloth cut in step 3 to a pre-heated mold, and heat pressing the glass fiber cloth cut in step 3 to obtain the product of a shoe insole. |