HIGH-STRENGTH ALUMINUM ALLOY THIN EXTRUDED SHAPE AND METHOD FOR PRODUCING THE SAME |
摘要 |
An Al—Zn—Mg—Cu-based high-strength aluminum alloy thin extruded shape has a yield strength of 700 MPa or more. The high-strength aluminum alloy thin extruded shape includes 9.0 to 13.0 mass % of Zn, 2.0 to 3.0 mass % of Mg, 1.0 to 2.0 mass % of Cu, and 0.05 to 0.3 mass % of Zr, with the balance being Al and unavoidable impurities, fine precipitates having a circle equivalent diameter of 5 to 20 nm being dispersed in a crystal grain of the extruded shape in a number of 4000 to 6000 per μm2. |
申请公布号 |
US2015059934(A1) |
申请公布日期 |
2015.03.05 |
申请号 |
US201414472902 |
申请日期 |
2014.08.29 |
申请人 |
UACJ Corporation |
发明人 |
SHINZATO Yoshifumi;HATTA Hidenori |
分类号 |
C22F1/053;C22C21/10 |
主分类号 |
C22F1/053 |
代理机构 |
|
代理人 |
|
主权项 |
1. A high-strength aluminum alloy thin extruded shape comprising 9.0 to 13.0 mass % of Zn, 2.0 to 3.0 mass % of Mg, 1.0 to 2.0 mass % of Cu, and 0.05 to 0.3 mass % of Zr, with the balance being Al and unavoidable impurities, fine precipitates having a circle equivalent diameter of 5 to 20 nm being dispersed in a crystal grain of the extruded shape in a number of 4000 to 6000 per μm2. |