摘要 |
<p>The present invention provides a cerium oxide based composite polishing powder and a preparation method thereof. The polishing powder contains the element magnesium in an amount of 0.005 wt %-5 wt % to magnesium oxide meter. The preparation method includes: (1) uniformly mixing a salt solution containing cerium serving as the main component of the polishing powder; (2) uniformly mixing a precipitating agent of an aqueous magnesium bicarbonate solution with the mixed solution prepared in step (1) to obtain a slurry; (3) aging the slurry prepared in step (2) for 0-48 h while the temperature of the slurry is kept at 30-90 degrees centigrade, and filtering the aged slurry to obtain the precursor powder of the polishing powder; (4) calcinating the precursor powder at 600-1000 degrees centigrade, then dispersing and separating the calcinated precursor powder to obtain the polishing powder. The present invention improves the polishing performance and the suspension performance of polishing powder.</p> |