发明名称 |
Fire-resistant piping material |
摘要 |
It is an object to provide a fire-resistant piping material that can be fire-protection measures by itself and is excellent in construction workability. A single-layered fire-resistant piping material according to the present invention is constituted of a fire-resistant resin composition containing heat-expandable graphite in an amount of 1 to 10 parts by weight based on 100 parts by weight of a polyvinyl chloride-based resin. A multilayered fire-resistant piping material according to the present invention includes a tubular fire-resistant expandable layer made of a heat-expandable fire-resistant resin composition and a covering layer covering at least one of the outer surface and the inner surface of the fire-resistant expandable layer, and the fire-resistant expandable layer is formed of a fire-resistant resin composition containing heat-expandable graphite in an amount of 1 to 15 parts by weight based on 100 parts by weight of a polyvinyl chloride-based resin, and the covering layer is formed of a polyvinyl chloride-based resin composition not containing heat-expandable fire-resistant materials. |
申请公布号 |
US8962115(B2) |
申请公布日期 |
2015.02.24 |
申请号 |
US200712733359 |
申请日期 |
2007.08.29 |
申请人 |
Sekisui Chemical Co., Ltd. |
发明人 |
Okabe Masashi;Ichihara Koji;Kimura Hideharu;Sanni Toshifumi |
分类号 |
F16L11/12;C08K3/04;B32B1/08;B32B27/18;B32B27/30;F16L5/04;F16L55/10;F16L59/14;C08L27/06 |
主分类号 |
F16L11/12 |
代理机构 |
Wenderoth, Lind & Ponack, L.L.P. |
代理人 |
Wenderoth, Lind & Ponack, L.L.P. |
主权项 |
1. A fire-resistant pipe, comprisinga pipe wall having a hollow tubular interior space for conveying a fluid therethrough,
wherein the pipe wall consists of a triple layer construction, wherein the pipe wall comprises
a tubular fire-resistant expandable layer made of a heat-expandable fire-resistant polyvinyl chloride-based resin composition,a covering layer covering the outer surface of the fire-resistant expandable layer, anda covering layer covering the inner surface of the fire-resistant expandable layer,wherein the fire-resistant expandable layer comprises
a fire-resistant polyvinyl chloride-based resin composition containing a heat-expandable graphite having
an expansion volume in the range of 100 to 250 mL/g and a 1.3-time expansion temperature of 180 to 240° C. in an amount of 1 to 15 parts by weight based on 100 parts by weight of the polyvinyl chloride-based resin; andwherein the covering layers comprise
a polyvinyl chloride-based resin composition not containing heat-expandable fire-resistant materials, and wherein the pipe wall has a tensile strength of 30 MPa or greater,wherein,
when the pipe is subjected to a fire-resistant test complying with ISO 834-1,
wherein the pipe is passed through a flooring material,wherein the underside of the flooring material is heated,wherein one end of the pipe is exposed to a heated side by 300 mm from the surface on the heated side of the flooring material, andwherein the other end of the pipe is exposed to a non-heated side by 800 mm from the surface on the non-heated side of the flooring material, the inner cross-sectional area S1 at the end of the pipe on the heated side and the inner cross-sectional area S2 at a minimum inner diameter of the pipe after burning satisfy the relationship:
(S2/S1)×100≦50. |
地址 |
Osaka JP |