METHOD FOR MANUFACTURING HIGH STRENGTH GALVANIZED STEEL SHEET AND HIGH STRENGTH GALVANIZED STEEL SHEET

摘要

A method for manufacturing a high strength galvanized steel sheet and a high strength galvanized steel sheet are provided. A base steel sheet having a chemical composition comprising C: 0.03% to 0.35%, Si: 0.01% to 0.50%, Mn: 3.6% to 8.0%, Al: 0.001% to 1.000%, P≦0.10%, S≦0.010%, and the balance comprising Fe and incidental impurities, on a percent by mass basis, is subjected to annealing and galvanization treatment, wherein the maximum steel sheet temperature in an annealing furnace is 600° C. or higher and 700° C. or lower, the steel sheet transit time in a temperature region of the maximum steel sheet temperature of 600° C. or higher and 700° C. or lower is specified to be 30 seconds or more and 10 minutes or less, and the dew point in an atmosphere is specified to be −45° C. or lower.

主权项

1. A method for manufacturing a high strength galvanized steel sheet having a zinc coating layer with an amount of deposition of coating of 20 to 120 g/m2 per one surface on the surface of a base steel sheet having a chemical composition comprising C, 0.03% to 0.35%, Si: 0.01% to 0.50%, Mn: 3.6% to 8.0%, Al: 0.001% to 1.000%, P≦0.10%, S≦0.010%, and the balance comprising Fe and incidental impurities, on a percent by mass basis, the method comprising the step of subjecting the base steel sheet to annealing and galvanization treatment in a continuous galvanizing line, wherein:
the maximum steel sheet temperature in an annealing furnace is 600° C. or higher and 700° C. or lower, and the steel sheet transit time in a temperature region of the maximum steel sheet temperature of 600° C. or higher and 700° C. or lower is specified to be 30 seconds or more and 10 minutes or less, and the dew point in an atmosphere is specified to be −45° C. or lower.