发明名称 |
Perovskite catalyst and method of manufacturing the same |
摘要 |
A method of manufacturing a perovskite catalyst composed of perovskite oxide includes mixing step, firing step and acid-treating step. In the mixing step, an A-site material and a B-site material are mixed at a stoichiometric ratio such that the A-site is increased, compared to that of a theoretical composition ABO3 of perovskite oxide in which a ratio of A-site and B-site is 1:1. In the firing step, the obtained mixed powder is fired. In the acid-treating step, the obtained fired powder is acid-treated with acid of pH 2 or more and less than pH 7. |
申请公布号 |
US8951932(B2) |
申请公布日期 |
2015.02.10 |
申请号 |
US201113299833 |
申请日期 |
2011.11.18 |
申请人 |
Denso Corporation |
发明人 |
Yoshii Takeshi;Nakanishi Tomohiko |
分类号 |
B01J21/00;B01J23/00;B01J25/00;B01J29/00;B01J23/10;C01B13/18;C01B13/14;C01G45/12;C01G49/00;C01G51/00;B01J37/24;B01J23/889;B01J23/83;B01J35/10;B01J37/22 |
主分类号 |
B01J21/00 |
代理机构 |
Nixon & Vanderhye P.C. |
代理人 |
Nixon & Vanderhye P.C. |
主权项 |
1. A perovskite catalyst manufactured by a method of manufacturing a perovskite catalyst, the method comprising the steps of:
first, mixing an A-site material and a B-site material at a stoichiometric ratio to obtain a mixed powder of A-site material and B-site material, the A-site being produced from A-site material, the B-site being produced from B-site material, the stoichiometric ratio being such that the A-site is greater than an A-site of a theoretical composition ABO3 of perovskite oxide in which a ratio between A-site and B-site is 1:1; second, firing the obtained mixed powder to obtain a fired powder; and third, acid-treating the obtained fired powder with acid of pH 2 or more and less than pH 7. |
地址 |
Kariya JP |