Polycarbonate resin composition and molded article |
摘要 |
To provide a polycarbonate resin composition excellent in flame resistance, impact resistance and external appearance and a molded article formed from the polycarbonate resin composition. The composition comprises 0.001 to 2 parts by mass of a metal organic sulfonate (B), 0.001 to 1 parts by mass of a fluoropolymer (C), 0.5 to 5 parts by mass of polyalkylsilsesquioxane particles having an average particle diameter of 0.6 to 5 μm (D), and 0.5 to 8 parts by mass of a graft copolymer (E) having a butadiene content ratio of 50% to 90%, relative to 100 parts by mass of a polycarbonate resin (A). |
申请公布号 |
US8927636(B2) |
申请公布日期 |
2015.01.06 |
申请号 |
US201013120383 |
申请日期 |
2010.09.08 |
申请人 |
Mitsubishi Engineering-Plastics Corporation |
发明人 |
Monden Toshiki |
分类号 |
C08L69/00;C08K5/42;C08L27/12;C08L51/06;C08L83/04;H01M2/02;C08L51/04 |
主分类号 |
C08L69/00 |
代理机构 |
Birch, Stewart, Kolasch & Birch, LLP |
代理人 |
Birch, Stewart, Kolasch & Birch, LLP |
主权项 |
1. A polycarbonate resin composition comprising 100 parts by mass of a polycarbonate resin (A), 0.001 to 2 parts by mass of a metal organic sulfonate (B), 0.001 to 1 parts by mass of a fluoropolymer (C), 0.5 to 4 parts by mass of polyalkylsilsesquioxane particles (D) having a volume-average particle diameter of 0.6 to 5 μm, 0.5 to 4.5 parts by mass of a graft copolymer (E) having a butadiene content ratio of 50% to 90%, and 0.0001 to 3 parts by mass of a carbon black (F), relative to 100 parts by mass of the polycarbonate resin;
wherein when the polycarbonate resin composition is injection-molded under a condition of a cylinder temperature of 290° C. and a mold temperature of 80° C. using an injection molding machine and formed to a test piece for ASTM tensile impact test having a thickness of 3.2 mm in accordance with ASTM D1822 Type S, and the test piece for ASTM tensile impact test was treated at 100° C. for 1000 hours, the tensile impact strength for the treated piece under the ASTM tensile impact test in accordance with ASTM D1822 is not less than 280 kJ/m2. |