| 摘要 |
The present invention provides a polycarbonate resin composition for molding a molded article having a thin-walled section and exhibiting a high level of flame resistance and impact resistance, and an excellent surface appearance (low-gloss property). More specifically, the present invention is a polycarbonate resin composition for molding a polycarbonate resin molded article having a thin-walled section with a wall thickness of 0.6 mm or less, the polycarbonate resin composition being characterized in that the resin composition contains an oligomeric phosphoric acid ester flame retardant (B1) and/or a phosphazene flame retardant (B2), and the content of flame retardant with respect to 100 parts by mass of polycarbonate resin (A) is: i) 5 to 20 parts by mass when the resin composition contains only the oligomeric phosphoric acid ester flame retardant (B1); ii) 10 to 30 parts by mass when the resin composition contains only the phosphazene flame retardant (B2); or iii) a total of 5 to 30 parts by mass when the resin composition contains both the oligomeric phosphoric acid ester flame retardant (B1) and the phosphazene flame retardant (B2), with the content ratio thereof being 1 to 49 mass% of (B1) and 99 to 51 mass% of (B2), the resin composition additionally contains 3 to 15 parts by mass of a siloxane-based core/shell elastomer (C) and 0.8 to 10 parts by mass of carbon black (D) with respect to 100 parts by mass of polycarbonate resin (A), the siloxane-based core/shell elastomer (C) has a silicon content of 9.1 to 30 mass% and a number-average particle size in the range of 50 to 1,000 nm, and the flow rate per unit time of the resin composition is 15 to 50 × 10 -2 cm 3 /sec. |