发明名称 |
Clinker substitute based on calcined clay |
摘要 |
A method for producing a clinker substitute for use in cement production includes predrying clay with an iron content >1.5 wt-% in a form of iron oxides and a kaolinite content <40 wt-% to a moisture <10 wt-%. The clay is comminuted to a grain size <2 mm. The clay is calcined by thermal treatment in a furnace at a temperature of 600 to 1000° C. The clay is thermally treated under reducing conditions at a temperature of 600 to 1000° C. so as to form a reduction product. The reduction product is intermediately cooled to a temperature <300° C. and finally cooled. |
申请公布号 |
US8906155(B2) |
申请公布日期 |
2014.12.09 |
申请号 |
US201214005280 |
申请日期 |
2012.02.24 |
申请人 |
Outotec Oyj |
发明人 |
Gasafi Edgar;Missalla Michael |
分类号 |
C04B7/13;C04B14/10;C04B20/04;C04B28/04;C04B7/52;C04B7/40;C04B111/00 |
主分类号 |
C04B7/13 |
代理机构 |
Leydig, Voit & Mayer, Ltd. |
代理人 |
Leydig, Voit & Mayer, Ltd. |
主权项 |
1. A method for producing a clinker substitute for use in cement production, the method comprising:
a) predrying clay with an iron content >1.5 wt-% in a form of iron oxides and a kaolinite content <40 wt-% to a moisture <10 wt-%; b) comminuting the clay to a grain size <2 mm; c) calcining the clay by thermal treatment in a furnace at a temperature of 600 to 1000° C.; d) thermally treating the clay under reducing conditions at a temperature of 600 to 1000° C. so as to form a reduction product; e) intermediately cooling the reduction product to a temperature <300° C.; and f) finally cooling the reduction product. |