发明名称 |
GOLF BALL AND METHOD FOR MANUFACTURING THE SAME |
摘要 |
A method for manufacturing a golf ball showing a great flight distance on driver shots for includes the steps of: preparing a rubber composition containing a base rubber, an α,β-unsaturated carboxylic acid having 3 to 8 carbon atoms and/or a metal salt thereof as a co-crosslinking agent, a crosslinking initiator and a carboxylic acid and/or a salt thereof; heat pressing the rubber composition at a press temperature ranging from t-40° C. to t-15° C. to mold a spherical core, wherein t ° C. is a one-minute half-life temperature of the crosslinking initiator; and forming at least one cover layer covering the spherical core. |
申请公布号 |
US2014357408(A1) |
申请公布日期 |
2014.12.04 |
申请号 |
US201414292306 |
申请日期 |
2014.05.30 |
申请人 |
DUNLOP SPORTS CO., LTD. |
发明人 |
SHINDO Ayaka;MIKURA Chiemi;SAKAMINE Ryota;GOJI Sho |
分类号 |
A63B37/00;B29C43/18;B29C43/00;A63B45/00 |
主分类号 |
A63B37/00 |
代理机构 |
|
代理人 |
|
主权项 |
1. A method for manufacturing a golf ball that comprises a spherical core and at least one cover layer covering the spherical core, comprising the steps of:
preparing a rubber composition containing a base rubber, an α,β-unsaturated carboxylic acid having 3 to 8 carbon atoms and/or a metal salt thereof as a co-crosslinking agent, a crosslinking initiator and a carboxylic acid and/or a salt thereof, provided that the rubber composition further contains a metal compound in the case of containing only the α,β-unsaturated carboxylic acid having 3 to 8 carbon atoms as the co-crosslinking agent; heat pressing the rubber composition at a press temperature ranging from t-40° C. to t-15° C. to mold the spherical core, wherein t ° C. is a one-minute half-life temperature of the crosslinking initiator; and forming at least one cover layer covering the spherical core. |