Process for coating discrete articles with a zinc-based alloyed layer

摘要

The present disclosure concerns a process suitable for coating discrete articles with a zinc-rich, fully alloyed layer. A known method for the corrosion-protection of such articles comprises the steps of hot-dip galvannealing, typically followed by painting. This hot-dip process has however to be performed at a high temperature, thereby submitting the articles to severe thermal stress. A novel vacuum deposition process of Zn is therefore presented. It is characterized in that, in the step of contacting the article with metallic Zn vapor, the temperature of the article is equal to or higher than the dew point of the Zn vapor. The process results in a coating having a uniform thickness, even on less accessible surfaces. The surface roughness is well adapted for the adhesion of paint.

主权项

1. A batch process for coating an iron or steel article with a Zn—Fe intermetallic layer, comprising:
providing a sealable furnace, comprising a process chamber equipped with a heating component, a component for introducing and extracting gasses, and access ports for the article to be coated; taking the article to be coated into the process chamber; contacting the article at a temperature of 200 to 650° C. with a reducing gas in the process chamber, thereby removing surface oxidation; extracting gasses from the process chamber to a residual pressure of less than 1000 Pa; contacting the article at a temperature of 225 to 650° C. with metallic Zn vapor in the process chamber, thereby coating the article with a Zn—Fe intermetallic layer; retrieving the coated article from the process chamber; wherein when contacting the article with metallic Zn vapor, the temperature of the article is equal to or higher than the dew point of the Zn vapor.