| 摘要 |
<p><P>PROBLEM TO BE SOLVED: To provide a lubrication-treated steel sheet for plastic working, capable of preventing seizing/die-galling in a multistage pressing under high contact pressure without a reactive soap treatment that takes a long time. <P>SOLUTION: Island-like zinc phosphate crystals and a lubrication film that covers the crystals are formed on the surface of a steel sheet. The lubrication film comprises a binder and a lubrication component, and≥50 mass% of the binder is an inorganic binder. The adhesion amount of the island-like zinc phosphate crystals is≥1.5 g/m<SP POS="POST">2</SP>and≤6.0 g/m<SP POS="POST">2</SP>, and the adhesion amount of the lubrication film is≥2.0 g/m<SP POS="POST">2</SP>and 6.0 g/m<SP POS="POST">2</SP>. The cross-sectional thickness of a mix layer that corresponds to a part where the gap between the island-like Zn phosphate crystals is filled with the lubrication film is≥0.3μm. <P>COPYRIGHT: (C)2013,JPO&INPIT</p> |