Particles comprising composite of para-aramid and additive material

摘要

The invention pertains to a method for making a polymer-additive composite particle from a dope by jet spinning the dope to obtain a pulp, fibril or fibrid, wherein the solvent of the dope is selected from N-methyl-2-pyrrolidone, N,N′-dimethylformamide, N,N′-dimethylacetamide, tetramethylurea, and 4 to 75 wt % of a composition consisting of 2 to 95 wt % of a para-aramid polymer and 5-98 wt % of a solid additive material, to a total of 100 wt %, and wherein the aramid polymer is dissolved in the solvent; or coagulating the dope by means of a rotor-stator apparatus in which the polymer solution is applied through the stator on the rotor so that the precipitating polymer-additive composite particle is subjected to shear forces while they are in a plastic deformable stage.

主权项

1. A polymer-additive material composite particle, wherein the composite particle is pulp, fibril or fibrid, and wherein the composite particle is obtained from a dope in a method comprising:
i) jet spinning the dope through a jet spin nozzle to obtain the pulp, fibril or fibrid, the dope including (a) a solvent that is selected from the group consisting of N-methyl-2-pyrrolidone, N,N′-dimethylformamide, N,N′-dimethylacetamide, tetramethylurea, and mixtures thereof; and (b) 4 to 75 wt % of a composition consisting of a para-aramid polymer and further a non-fibrous, non-aramid solid additive, the para-aramid polymer being present in the composition in an amount of 2 to 80 wt % and the non-fibrous, non-aramid solid additive being present in the composition in an amount of 20 to 98 wt %; wherein the para-aramid polymer is dissolved in the solvent; or ii) coagulating the dope to obtain the pulp, fibril or fibrid by means of a rotor-stator apparatus, in which the dope is applied through the stator on the rotor so that polymer-additive composite pulp, fibril or fibrid are precipitated and subjected to shear forces while the polymer-additive composite pulp, fibril or fibrid are in a plastic deformable stage, wherein said pulp, fibril or fibrid comprises a para-aramid polymer and a solid additive, the dope including (a) a solvent that is selected from the group consisting of N-methyl-2-pyrrolidone, N,N′-dimethylformamide, N,N′-dimethylacetamide, tetramethylurea, and mixtures thereof; and (b) 4 to 75 wt % of a composition consisting of a para-aramid polymer and further a non-fibrous, non-aramid solid additive, the para-aramid polymer being present in the composition in an amount of 2 to 80 wt % and the non-fibrous, non-aramid solid additive being present in the composition in an amount of 20 to 98 wt %; wherein the para-aramid polymer is dissolved in the solvent; wherein, based on dry weight, the composite particle comprises 2 to 80 wt % of the para-aramid polymer and 20 to 98 wt % of the non-fibrous, non-aramid solid additive, wherein the para-aramid polymer is directly bonded to the non-fibrous, non-aramid solid additive such that the non-fibrous, non-aramid solid additive cannot be separated from the para-aramid polymer by filtration and washing, or any other mechanical or chemical separation procedure other than dissolving the para-aramid polymer in a solvent in which the non-fibrous, non-aramid solid additive is insoluble.