Method for concentrating and recovering precious metals from spent mobile phone PCBS and spent auto-catalysts using waste nonferrous slag

摘要

The present invention relates to a method of concentrating and recovering precious metals from waste mobile phone PCBs and spent automotive catalysts using waste nonferrous slag, in which precious metals such as gold, silver, platinum, palladium or rhodium can be concentrated and recovered by simultaneously treating different industrial wastes, including waste nonferrous slag, waste mobile phone PCBs and spent automotive catalysts, and industrial waste can be recycled as resources. According to the present invention, it is possible to maximize the utilization ratio of precious metal resources that totally depend on the import in terms of the domestic situation of a poor-natural resources country. In addition, the industrial waste can widely be utilized for the recovery of precious metals in the fields of household appliance recycling and electronic part manufacture, and the recycling of industrial by-products discharged in the field of non-ferrous refinery.

主权项

1. A method of concentrating and recovering precious metals from waste mobile phone PCBs (Printed Circuit Boards) and spent automotive catalysts using waste nonferrous slag, the method comprising the steps of:
(a) crushing waste nonferrous slag; (b) crushing spent automotive catalysts; (c) uniformly mixing caustic lime (CaO), which is a flux for controlling slag composition, with the waste nonferrous slag resulting from step (a) thereby forming a mixture, wherein the caustic lime is present in an amount of 5 to 40 parts by weight based on 100 parts by weight of the waste nonferrous slag, the mixture being charged into an electric furnace, followed by melting at a temperature of from 1300 to 1450° C. for 10 to 20 minutes; (d) introducing waste mobile phone PCBs and the spent automotive catalysts of step (b) into the melt of step (c), followed by melting; and (e) maintaining the melt of step (d) for a predetermined time to separate the melt into an alloy phase containing precious metals and a slag phase containing no precious metal.