High abrasion resistance coating process

摘要

A process for coating a front and back surface of an industrial textile to increase its abrasion resistance is disclosed. The coating process comprises the steps of coating the textile with a coating compound, heating coated textile at a temperature of 120 degree Celsius and drying the coated textile for 60 seconds. Two passes of coating is applied for the process wherein the viscosity for first pass of coating is 21000 centipoise and the viscosity for second pass of coating is 12000 centipoise. On completion of the coating process, the coated textile is treated with a water repellent agent. The coating compounds used for the process are comprised of formulations including two polyurethane compositions, which are mixed with a methyl ethyl ketone solvent, and the water repellent agent is silicone. The overall process requires a curing time of 2 minutes with a curing agent.

主权项

1. A process for coating a front and back surface of an industrial textile to increase abrasion resistance thereof, the process comprising the steps of:
(a) providing a first pass of coating of the textile applied at a speed of 45 inches/minute, wherein viscosity is 21000 centipoise, comprising:
(i) a coating compound having a formulation including the following: 120 grams of a first polyurethane compound, 30 grams of a second polyurethane compound, and 5 grams of methyl ethyl ketone solvent, to provide high abrasion resistance for the textile at least three times the normal industry standard; (b) providing a second pass of coating of the textile applied at a speed of 45 inches/minute, wherein viscosity is 12000 centipoise; (c) heating and drying the textile after each coating at a heating temperature of 120 degrees Celsius with a drying time of 60 seconds; (d) treating the coated textile with the water repellent agent, silicone; and (e) curing the coated textile for a period of 2 minutes.