Crosslinkable polyolefin composition comprising silane groups forming an acid or a base upon hydrolysation

摘要

The present invention relates to a polyolefin composition comprising (A) a crosslinkable polyolefin with hydrolysable silane groups which upon hydrolysation form an acid or a base, characterised in that the acid or base generates a gel content of at least 40% after 40 hours in the 90° C. cross-linking test, wherein the acid or base is added in an amount of 4.5 mmol/kg to an ethylene/vinyltrimethoxysilane copolymer with a MFR2=2 g/10 min, a density of 923 g/cm3, and 2 wt. % of vinyltrimethoxysilane and then is cross-linked in a waterbath at 90° C., and to a polyolefin composition comprising (i) a crosslinkable polyolefin with hydrolysable silane groups, and (ii) a non-polymeric compound with hydrolysable silane groups which upon hydrolysation form an acid or a base, characterised in that the acid or base generates a gel content of at least 40% after 40 hours in the 90° C. cross-linking test, wherein the acid or base is added in an amount of 4.5 mmol/kg to an ethylene/vinyltrimethoxysilane copolymer with a MFR2=2 g/10 min, a density of 923 g/cm3, and 2 wt. % of vinyltrimethoxysilane and then is cross-linked in a waterbath at 90° C.

主权项

1. A polyolefin composition comprising
(i) a crosslinkable polyolefin with hydrolysable silane groups, the crosslinkable polyolefin being prepared from a hydrolysable silane compound represented by Formula (II):
CH2═CHSi(OA)3  (II)wherein A is a hydrocarbyl group having 1-8 carbon atoms; and
(ii) a non-polymeric compound with hydrolysable silane groups which upon hydrolysation form an acid or a base, wherein the non-polymeric compound has 50 repeating units or less, and is represented by Formula (III):
R1SiR2R3R4  (III) wherein R1 is a non-hydrolysable hydrocarbyl group which comprises 2 to 30 carbon atoms, which further comprises at least one unsaturated group, and optionally contains heteroatoms; and R2, R3, and R4 are organic residues which may be the same or different from each other with the proviso that at least one thereof is an acyloxy group that will generate a carboxylic acid upon hydrolysation or is an amino group that will generate an amine upon hydrolysation; characterised in that the carboxylic acid or amine is one which generates a gel content of at least 40% after 40 hours in a 90 ° C. cross-linking test which is conducted as follows: a copolymer of ethylene and vinyltrimethoxysilane having a MFR2 (2.16 kg, 190° C.) of 2 g/10 min, a density of 923 g/cm3, and 2 wt.% of vinyltrimethoxysilane is provided, to which the carboxylic acid or amine is added in an amount of 4.5 mmol/kg to form a crosslinkable composition, said crosslinkable composition is formed to a tape of 1.7 mm thickness, and said tape is cross-linked in a waterbath at a temperature of 90 ° C.