A microwave energy interactive structure includes a polymer film having a crystallinity of from about 1% to about 50% (as derived from density measurements) prior to being exposed to microwave energy, and a layer of microwave energy interactive material on the polymer film. The layer of microwave energy interactive material is operative for converting at least a portion of impinging microwave energy into thermal energy.