发明名称 |
Calcium hydroxide, resin composition containing the same, and molded article containing the composition |
摘要 |
There are provided calcium hydroxide having a large specific surface area, a resin composition comprising the calcium hydroxide and having excellent thermal stability, and a molded article and a stabilizer for synthetic resins which comprise the calcium hydroxide.;There are provided a calcium hydroxide compound represented by the following formula (1):
Ca(OH)2-nx(An−)x (1)
(wherein n represents an integer of 1 to 4, x represents a number of 0.001 to 0.2, and An− represents an anion derived from at least one compound selected from the group consisting of a silicon-based compound, a phosphorus-based compound, an aluminum-based compound, an inorganic acid and an organic acid.),
and a synthetic resin, a molded article and a stabilizer for synthetic resins which comprise the compound. |
申请公布号 |
US8809439(B2) |
申请公布日期 |
2014.08.19 |
申请号 |
US200410579389 |
申请日期 |
2004.11.11 |
申请人 |
Kyowa Chemical Industry Co., Ltd. |
发明人 |
Suzuki Takafumi;Matsushima Masatoshi;Miyauchi Seiji;Manabe Hitoshi;Sawa Yoshiharu |
分类号 |
C08K3/10;C08K9/10;C01F11/02;C04B26/02;C08K3/22;C09C1/02;C04B22/06 |
主分类号 |
C08K3/10 |
代理机构 |
Wenderoth, Lind & Ponack, L.L.P. |
代理人 |
Wenderoth, Lind & Ponack, L.L.P. |
主权项 |
1. A resin composition comprising:
(i) 100 parts by weight of synthetic resin, (ii) 0.1 to 10 parts by weight of calcium hydroxide produced by reacting an aqueous solution of a water-soluble calcium salt with an aqueous solution of an alkali metal hydroxide in the presence of an organosilicon-based compound, wherein the water-soluble calcium salt is calcium chloride or calcium nitrate, and wherein the alkali metal hydroxide is sodium hydroxide or potassium hydroxide,
wherein the calcium hydroxide:(a) is represented by the following formula (1):
Ca(OH)2-nx(An−)x (1)wherein n is 4, x represents a number of 0.001 to 0.2, and An− is SiO44−,(b) has an average secondary particle diameter, measured by a laser diffraction scattering method, of 0.1 to 7 μm, and(c) has a BET method specific surface area of 5 to 40 m2/g, and (iii) 0.1 to 10 parts by weight of hydrotalcite represented by the following formula (2):
{(Mg)y(Zn)z}1-x(Al)x(OH)2(An−)x/n.mH2O (2)wherein An− represents ClO4−, SO42−, CO32− or a mixture thereof, n is 1 or 2, and x, y, z and m satisfy y+z=1, 0.1<x<0.5, 0.5<y<1, 0≦z<0.5 and 0<m<1). |
地址 |
Kagawa JP |