HIGH-STRENGTH GALVANIZED STEEL SHEET EXCELLENT IN BENDABILITY AND MANUFACTURING METHOD THEREOF

摘要

The present invention provides a high-strength galvanized steel sheet with maximum tensile strength of 900 MPa or more. The high-strength galvanized steel sheet has an alloyed galvanized layer formed on a surface of a base steel sheet containing predetermined amounts of C, Si, Mn, P, S, Al, N, O with a balance being constituted of iron and inevitable impurities, in which in a structure of the base steel sheet, retained austenite is limited to 8% or less in volume fraction, kurtosis K* of the hardness distribution between 2% hardness and 98% hardness is −0.30 or less, a ratio between Vickers hardness of surface layer of the base steel sheet and Vickers hardness of ¼ thickness of the base steel sheet is 0.35 to 0.70, and a content of iron in the alloyed galvanized layer is 8 to 12% in mass %.

主权项

1. A high-strength galvanized steel sheet excellent in bendability with maximum tensile strength of 900 MPa or more, comprising an alloyed galvanized layer formed on a surface of a base steel sheet containing, in mass %,
C: 0.075 to 0.300%, Si: 0.30 to 2.50%, Mn: 1.30 to 3.50%, P: 0.001 to 0.050%, S: 0.0001 to 0.0100%, Al: 0.005 to 1.500%, N: 0.0001 to 0.0100%, and O: 0.0001 to 0.0100% with a balance being constituted of iron and inevitable impurities, wherein: retained austenite is limited to 8% or less in volume fraction in a range of ⅛ thickness to ⅜ thickness of the base steel sheet; when plural measurement regions with a diameter of 1 μm or less are set in the range of ⅛ thickness to ⅜ thickness of the base steel sheet, measurement values of hardness in the plural measurement regions are arranged in an ascending order to obtain a hardness distribution, an integer N0.02 is obtained, which is a number obtained by multiplying a total number of measurement values of hardness by 0.02 and rounding up this number when this number includes a fraction, hardness of a measurement value which is N0.02-th largest from a measurement value of minimum hardness is taken as 2% hardness, an integer N0.98 is obtained, which is a number obtained by multiplying a total number of measurement values of hardness by 0.98 and rounding down this number when this number includes a fraction, and hardness of a measurement value which is N0.98-th largest from a measurement value of minimum hardness is taken as 98% hardness, kurtosis K* of the hardness distribution between the 2% hardness and the 98% hardness is −0.30 or less; a ratio between Vickers hardness of surface layer of the base steel sheet and Vickers hardness of ¼ thickness of the base steel sheet is 0.35 to 0.70; and a content of iron in the alloyed galvanized layer is 8 to 12% in mass %.