Flat container comprising thermoplastic resin and method for molding the same

摘要

The invention realizes easy manufacturing of a flat container molded by blow molding, in which the wall thickness of a container wall is made uniform, and which provides improved mechanical strength, heat resistance, etc. and has a good appearance.;The flat container obtained by the blow molding of a polyester resin is characterized in that the container has a flatness ratio of not less than 1.3, and in that its body has a wall thickness ratio of a maximum wall thickness to a minimum wall thickness of not more than 1.6, a difference in elongation between a maximally stretched portion and a minimally stretched portion of not more than 150% in a tensile test at 95° C., a crystallinity of not less than 30%, and a difference in TMA non-load change between a maximally stretched portion and a minimally stretched portion of not more than 500 μm at 75° C. and 100° C.

主权项

1. A flat polyester resin container comprising polyester resin and obtained by a two-stage blow molding of a polyester resin,
wherein the flatness ratio, which is the ratio of a major axis to a minor axis of a cross section parallel to the bottom of the container, is not less than 1.3, the wall thickness ratio of a maximum wall thickness to a minimum wall thickness of a body of the container is not more than 1.6, a difference in elongation between a maximally stretched portion and a minimally stretched portion of the body of the container in a tensile test at 95° C. is not more than 150%, the crystallinity of the body of the container is not less than 30%, and a difference in TMA non-load change between a maximally stretched portion and a minimally stretched portion of the body of the container at 75° C. and 100° C. is not more than 500 μm, wherein the flat polyester resin container is obtained by a process comprising:
subjecting a bottomed parison preformed from a polyester resin to primary blow molding, thereby molding the bottomed parison into a bottomed cylindrical body having a diameter larger than the minor axis of a cavity within a mold for secondary blow molding, thereaftercausing the bottomed cylindrical body to shrink in a heated condition, thereby to cause the bottomed cylindrical body to maintain a diameter which is smaller than the major axis of the cavity within the mold for secondary blow molding and larger than the minor axis thereof,attaching the bottomed cylindrical molded article to the interior of the mold for secondary blow molding and performing mold clamping, with the bottomed cylindrical molded article depressed in a flat condition in the minor axis direction of the cavity within the mold for secondary blow molding, so that the major axis portion of the bottomed cylindrical body does not come into contact with mold surfaces,feeding thereafter a pressure fluid into the bottomed cylindrical molded article, and causing the bottomed cylindrical molded article to flow in a heated condition along the shape of the cavity on an inner surface of the mold, thereby to mold the flat polyester resin container.