发明名称 |
Method to produce a hot formed part, and part thus formed |
摘要 |
The invention relates to a. method for manufacturing a coated steel part having very high mechanical properties using hot forming techniques. According to the invention, the method comprises the following steps:
€¢ providing a coated steel blank comprising a steel substrate with a coating layer
€¢ heating the blank to a temperature of 800° C or more in a furnace
€¢ transporting the heated blank from the furnace and placing the blank in a hot forming press
€¢ hot forming the blank in the press to form the coated steel part
€¢ quenching the coated steel part
wherein the heated blank has a temperature of at most 780° C when placed in the hot forming press. The invention also relates to a hot formed part manufactured using the method according to the invention. |
申请公布号 |
EP2754723(A2) |
申请公布日期 |
2014.07.16 |
申请号 |
EP20140163594 |
申请日期 |
2012.01.17 |
申请人 |
TATA STEEL IJMUIDEN BV |
发明人 |
VERLOOP, WILLEM CORNELIS;VAN GENDEREN, MARC JACCO;VAN TOL, RONALD THEODOOR;HENSEN, GUIDO CORNELIS |
分类号 |
C21D1/673;B21J1/06;B21J3/00;C21D1/02;C21D8/00;C21D9/46 |
主分类号 |
C21D1/673 |
代理机构 |
|
代理人 |
|
主权项 |
|
地址 |
|