Method of manufacturing optical waveguide

摘要

A mold for the formation of an over cladding layer in an optical waveguide is integrally produced from a light-transmissive resin and a light-transmissive support plate by molding using a mold member identical in shape with the over cladding layer. In the production of the mold, a hollow resulting from the removal of the mold member serves as a cavity for the formation of the over cladding layer. For the formation of the over cladding layer, the cavity of the mold is filled with a photosensitive resin for the formation of the over cladding layer, and the photosensitive resin is cured by being exposed to light through the mold while cores formed in a pattern on a surface of an under cladding layer are immersed in the photosensitive resin.

主权项

1. A method of manufacturing an optical waveguide, comprising:
forming a core having a pattern on a surface of an under cladding layer; and forming an over cladding layer so as to cover the core by using a mold including a cavity having a mold surface complementary in shape to the over cladding layer, wherein the forming of the over cladding layer includes:
placing the mold with the cavity of the mold positioned upwards,filling the cavity of the mold with a photosensitive resin for the formation of the over cladding layer,after the filling, immersing the core in the photosensitive resin, andexposing the photosensitive resin to light through the mold, with the core immersed in the photosensitive resin, to cure the photo sensitive resin, thereby forming the over cladding layer, wherein the mold is made of a light-transmissive resin and provided with a light-transmissive support plate, wherein mold is produced by placing a mold member identical in shape with the over cladding layer in a mold production container, filling the container with a light-transmissive resin, bringing the light-transmissive support plate into contact with a surface of the light-transmissive resin, curing the light-transmissive resin in that state, fixedly securing the cured light-transmissive resin to the light-transmissive support plate, then taking the cured light-transmissive resin out of the container, and removing the mold member from the cured light-transmissive resin, whereby a hollow resulting from the removal of the mold member serves as the cavity for the formation of the over cladding layer.