| 摘要 |
<p>The present invention is a laminate comprising a resin layer (A) obtained from a thermoplastic resin layer (A) and a resin layer (B) laminated on at least one side thereof and obtained from a different thermoplastic resin, wherein: (i) the thickness of the resin layer (B) is 40 - 150 µm, and the total thickness of the resin layer (A) and the resin layer (B) is 0.8 mm - 3.0 mm, (ii) the respective glass transition points TgA and TgB of the thermoplastic resin (A) and thermoplastic resin (B) are both 115°C or more and the difference between TgA and TgB is 30°C or less, (iii) the water absorption rates of the thermoplastic resin (A) and the thermoplastic resin (B) are both 0.7% or less and the difference in water absorption rates is 0.5% or less, and (iv) the warping rate after the resin laminate is left for 120 hours in a high temperature, high humidity environment of 85°C temperature and 85% RH humidity is 0.2% or less.</p> |