| 摘要 |
<p>Provided is a novel transparent adhesive sheet with which the cut edge is not sticky over time when a laminated body that has been bonded via the adhesive sheet is cut, which can be adhered without generating residual air bubbles, even when the surface of an adherend is uneven, and which can be adhered without foaming, even when the adherend is a material such as plastic that can generate outgas. Suggested is a transparent adhesive sheet for an image display device comprising:
one or more layers of a first adhesive layer; and
one or more layers of of a second adhesive layer,
wherein the first and second adhesive layers exhibit different viscoelastic behaviors and the layers are integrally laminated, and;
wherein the first adhesive layer is comprised of a composition comprising acrylic acid ester and cross-linking agents which are multifunctional organic functional group resins having two or more organic functional groups selected from an isocyanate group, an epoxy group, a melamine group, a glycol group, a siloxane groups and an amine group, and;
wherein a dynamic shear storage modulus G' (measured with use of a device for measuring viscoelasticity in a shear method under the conditions Jig: Φ25 mm parallel plate, strain level: 0.5%, frequency: 1 Hz, temperature: -70 to 200 °C (measured at 3 °C/min temperature elevation rate from -70 °C), sample thickness: 250 µm) as to the adhesive sheet integrally laminated is within the ranges described below when measured with a 1 Hz frequency temperature dispersion:
• G'(20°C) is 2 x 104 to 5 x 105 Pa; and
• G'(150°C) is 1 x 104 to 1 x 105 Pa.
</p> |