The present invention relates to a method for producing an ±-form titanylphthalocyanine represented by the formula (1):
which has a peak at a Bragg angle (2¸ ± 0.2°) in X-ray diffraction spectrum with CuK ±-ray: 7.5°, 10.2°, 12.6°, 13.2°, 15.1°, 16.3°, 17.3°, 18.3°, 22.5°, 24.2°, 25.3° and 28.6°, wherein the method includes steps of:
(I) subjecting a crude titanylphthalocyanine having an ±-form polymorph to an acid pasting treatment, and then filtering and washing with water to give a water-containing wet cake, and then subjecting the wet cake to drying and crushing to give a low crystalline titanylphthalocyanine;
(II) adding a dispersing aid to the low crystalline titanylphthalocyanine and dispersing at room temperature, in DMF, to prepare a polymorph; and
(III) filtering, washing, and drying under a reduced pressure. The present invention consists in a provision of a method for conveniently producing the ±-form titanylphthalocyanine having a peak at a Bragg angle (2¸ ± 0.2°) in X-ray diffraction spectrum with CuK ±-ray: 7. 5°, 10. 2°, 12. 6°, 13.2°, 15.1°, 16.3°, 17.3°, 18.3°, 22.5°, 24.2°, 25.3° and 28.6°, wherein a crude titanylphthalocyanine having an ±-form polymorph is used as a starting material, as well as a provision of an electrophotographic photoreceptor comprising a charge generating material of the ±-form titanylphthalocyanine which has excellent photosensitive characteristics. |