| 摘要 |
Provided in the present invention is a method for forming a plate-shaped metal-carbon nanotube complex using a planetary medium pulverizer, including a step of conducting a milling in which metal powder and carbon nanotube are combined, using the planetary medium pulverizer. The ratio of the pulverizing medium applied to the medium pulverizer and the metal powder and carbon nanotube is 10 to 1 by weight, and the diameter of the pulverizing medium can range from 3 to 10 mm. Moreover, the milling can be conducted for 4 to 70 minutes at an rpm ranging from 300 to 700. The metal powder takes up about 97 to 98 % by weight and the carbon nanotube about 2 to 3 % by weight in total. The metal powder can be one of any group chosen among Au, Ag, Cu, Al, Mn, Fe, Sn, Zn, and Ti, and more desirably Al. In addition, the carbon nanotube can be a mixture comprising one or two kinds of any group chosen from single-wall carbon nanotube, double-wall carbon nanotube, thin-multi-layered carbon nanotube, and multi-layered carbon nanotube, and the diameter ranging from 0.7 nm to 100μm, with a length ranging from 10 nm to 10 cm. [Reference numerals] (S10) Metal powder + carbon nanotube milling; (S20) Plate-shaped metal - carbon nanotube complex formation |