发明名称 |
Verfahren zur Wärmebehandlung einer Legierung auf Aluminiumgrundlage |
摘要 |
<p>Resistance to stress corrosion cracking is effected without noticeable reduction in strength or weight penalties by heating Al alloy contg. Cu, Mg and Zn to 460-477 degrees C for time sufficient to allow constituents to enter into solid soln., quenching with water and ageing by (a) first heating to 96-107 degrees C for 6-10 hrs., and then (b) to 149-193 degrees C for 2-48 hrs. Pref. alloy is cooled to room temp. before last heating step. Pref. (b) ageing step takes place by heating to 157-179 degrees C for 4-18 hrs.</p> |
申请公布号 |
CH500287(A) |
申请公布日期 |
1970.12.15 |
申请号 |
CH19650009199 |
申请日期 |
1965.07.01 |
申请人 |
HARVEY ALUMINIUM (INCORPORATED) |
发明人 |
CARLETON ROTSELL,WAYNE;RICHARD LONG,JAMES |
分类号 |
C22C21/00;C22C21/10;C22F1/053;(IPC1-7):C22F1/04 |
主分类号 |
C22C21/00 |
代理机构 |
|
代理人 |
|
主权项 |
|
地址 |
|