HIGH-TEMPERATURE PLASTIC ARTICLE

摘要

A plastic article having a thickness of 2 mm to 3.2 mm is disclosed. The article is formed from a thermoplastic composition that includes a first polymer that is a polycarbonate, a second polymer that is a polyphthalatecarbonate, a perfluoroakyl sulfonate salt; and a cyclic siloxane compound. The thermoplastic has a light transmittance at a thickness of 3.2 mm of at least 86% according to ASTM D1003-11E1, a UL94 flammability rating of V0, a notched Izod impact strength at a thickness of 3.2 mm of at least 500 J/m according to ASTM D256-05 with a 2.27 kg weight at a, and a heat deflection temperature at a thickness of 3.2 mm of at least 160°C according to ASTM D648-06 under a load of 0.45 MPa.